For precious metal coating up to 1,5µm:
Rhodium bath / rhodium electrolyte
Black rhodium bath JE23-1 GO! - 2 g/L Rh
The black rhodium bath JE23-1 deposits dark anthracite-grey, particular decorative rhodium coatings. The layers are very abrasion resistant, colour consistent and uniform. The electrolyte is preferably used for decorative coatings in the jewellery and eyewear industry. JE23-1 is characterized by it's easy handling and usability. It works at room temperature so a time and energy intensive heating-up can be omitted. Coatings up to 0,5 µm can be deposited. Operating Data:Rhodium content: 2,0 g/L RhpH-Value: <1Density: 1,02 – 1,07 g/cm3 Working conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 27°CExposition time: 2 min. (1 - 5 min.)Anodes: Platinized titanium, mixed-metal-oxideAnode/ Cathode: 1:1Current density: 1,0 - 1,5 A/dm2Agitation: required Deposition rate: 6 - 8mg/AminBath filtration: ab 10 LiterDeposition Data:Hardness: 300 - 370 HVLayer thickness: max. 0,5 μmLayer density: ca. 10,5 g/cm3Form of delivery:Ready for use
Black Rhodium Concentrate JE23-1 - 2g/100ml Rh
The black rhodium bath JE23-1 deposits dark anthracite-grey, particular decorative rhodium coatings. The layers are very abrasion resistant, colour consistent and uniform. The electrolyte is preferably used for decorative coatings in the jewellery and eyewear industry. JE23-1 is characterized by it's easy handling and usability. It works at room temperature so a time and energy intensive heating-up can be omitted. Coatings up to 0,5 µm can be deposited.Operating data:Rhodium content: 2,0 g/100ml RhpH-Value: <1Density: 1,02 - 1,07 g/cm3 Working conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 27°CExposition time: 2 min. (1 - 5 min.)Anodes: Platinized titanium, mixed-metal-oxideAnode/ Cathode: 1:1Current density: 1,0 - 1,5 A/dm2Agitation: requiredDeposition rate: 6 - 8mg/AminBath filtration: ab 10 LiterDeposition data:Hardness: 300 - 370 HVLayer thickness: max. 0,5 μmLayer density: ca. 10,5 g/cm3Form of delivery:Concentrate form 2 g/100ml Rh for 1 litre bathConcentrated bath preparation:Mix 100 ml of the Rhodium JE88 concentrate with 900 ml distilled water.
Rhodium bath JE88 CLEAN - 2 g/L Rh
The rhodium bath JE88 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. The color of JE88 CLEAN may vary in slight nuances as the product is produced exclusively from recycled rhodium. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 1,0 µm can be deposited.Operating data:Rhodium content: 2,0 g/L RhpH-Value: <1Operating conditions:Voltage: 2-3 VoltBath temperature: 20-35°CExposition time: 2 min. (1-max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1 : 1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 - 900 HVLayer thickness: max. 1,0 µmLayer density: approx. 12,4 g/cm3Form of delivery:-Ready for use 2 g/L Rh-Concentrate form 2 g/100ml Rh for 1 litre bath
Rhodium Bath JE88 GO! - 2 g/L Rh
The rhodium bath JE88 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 1 µm can be deposited.Operating data:Rhodium content: 2,0 g/L RhpH-Value: <1Operating conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 40 °CExposition time: 2 min. (1 - max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1:1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 - 900 HVLayer thickness: max. 1,0 µmLayer density: approx. 12,4 g/cm3Form of delivery:- Ready for use 2 g/L Rh- Concentrate form 2 g/100ml Rh for 1 litre bath
Rhodium Bath JE88 GO! NDG - 0,5 g/L Rh
The JE88! GO NDG rhodium bath represents a significant innovation in electroplating technology. It is the first rhodium that is not classified as a hazardous material during transportation, allowing for safe and easy worldwide shipping.This advanced rhodium is ideal for decorative coatings in the jewelry, eyeglass frame and watch industries. It also provides effective tarnish protection for silverware. With the ability to precisely deposit layers down to 1.0 µm, the JE88! GO NDG rhodium bath ensures exceptional brilliance and durability. Its versatility makes it the ideal choice for various electroplating applications.Operating Data: Rhodium content: 0,5 g/L pH-Value: <1 Working conditions: Voltage: 2,5 – 3,5 Volt Bath temperature: 20 - 30° C Exposition time: 2 min. (1 max. 10 min) Anodes: Platiniertes Titan oder Mischoxid MOX Anode/ Cathode: 1 : 1 Current density: 0,5 – 2,0 A/dm2 Agitation: advantageous Bath filtration: from 10 Liter Deposition rate: 6 – 8mg/Amin Form of Delivery: Ready for use 0,5 g/L
Rhodium Bath JE88 GO! NDG - 1 g/L Rh
The JE88! GO NDG rhodium bath offers a decisive advantage: it is the first rhodium that does not have to be declared as dangerous goods during transportation. This innovation enables problem-free and safe worldwide shipping.The revolutionary rhodium is ideal for decorative coatings with a small electroplating process in the jewelry, eyeglass frame and watch industries. It is also frequently used as effective tarnish protection for silverware. The precise deposition of layers of up to 1.0 µm enables outstanding brilliance and durability. The versatile application makes the JE88! GO NDG rhodium bath the ideal choice for various electroplating processes.Operating Data:Rhodium content: 1,0 g/LpH-Value: <1Working conditions:Voltage: 2,5 – 3,5 VoltBath temperature: 20 - 30° CExposition time: 2 min. (1 max. 10 min)Anodes: Platiniertes Titan oder Mischoxid MOXAnode/ Cathode: 1 : 1Current density: 0,5 – 2,0 A/dm2Agitation: advantageousBath filtration: from 10 LiterDeposition rate: 6 – 8mg/AminForm of Delivery:Ready for use 1,0 g/L
Rhodium Bath JE88 GO! NDG - 2 g/L Rh
The JE88! GO NDG rhodium bath offers a decisive advantage: it is the first rhodium that does not have to be declared as dangerous goods during transportation. This innovation enables problem-free and safe worldwide shipping.The revolutionary rhodium is ideal for decorative coatings with a small electroplating process in the jewelry, eyeglass frame and watch industries. It is also frequently used as effective tarnish protection for silverware. The precise deposition of layers of up to 1.0 µm enables outstanding brilliance and durability. The versatile application makes the JE88! GO NDG rhodium bath the ideal choice for various electroplating processes.Operating Data:Rhodium content: 2,0 g/LpH-Value: <1Working conditions:Voltage: 2,5 – 3,5 VoltBath temperature: 20 - 30° CExposition time: 2 min. (1 max. 10 min)Anodes: Platiniertes Titan oder Mischoxid MOXAnode/ Cathode: 1 : 1Current density: 0,5 – 2,0 A/dm2Agitation: advantageousBath filtration: from 10 LiterDeposition rate: 6 – 8mg/AminForm of Delivery:Ready for use 2,0 g/L
Rhodium bath JE88-1 CLEAN - 1 g/L Rh
The rhodium bath JE88-1 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. The color of the electrolyte in the bottle may vary slightly, as the product is made exclusively from recycled rhodium. However, this does not affect the color of the deposited rhodium layer. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 0,5 µm can be deposited. Operating data:Rhodium content: 1,0 g/L Rh pH-Value: < 1 Operating conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 40 °CExposition time: 2 min. (1 - max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1 : 1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 - 900 HV Layer thickness: max. 0,5 µm Layer density: approx. 12,4 g/cm3 Form of delivery:- Ready for use 1 g/L Rh - Concentrate form 1 g/100ml Rh for 1 litre bath
Rhodium bath JE88-1 GO! - 1 g/L Rh
The rhodium bath JE88-1 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 0,5 µm can be deposited.Operating data:Rhodium content: 1,0 g/L RhpH-Value: < 1Operating conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 40 °CExposition time: 2 min. (1 - max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1 : 1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 - 900 HVLayer thickness: max. 0,5 µmLayer density: approx. 12,4 g/cm3Form of delivery:- Ready for use 1 g/L Rh- Concentrate form 1 g/100ml Rh for 1 litre bath
Rhodium black JE29-1 for pen (1 g/50ml Rh)
The rhodium bath black for JE29-1 for pen is especially suitable for partial plating, for multi-colour processeing and reparation or restoration. The deposited coatings have a dark anthracite-grey colour and they are hard and abrasion resistant. JE29-1 deposits uniform rhodium layers and has a strong colour consistency.The plating layer created by pen plating is very thin. If you would like a thicker layer, we recommend that you treat the goods in a normal electroplating bath.Rhodium content: 1g Rh/50 mlVoltage: 6-10 VoltBath temperature: Room temperature
Rhodium black JE29-1 for pen (2 g/100ml Rh)
The rhodium bath black for JE29-1 for pen is especially suitable for partial plating, for multi-colour processeing and reparation or restoration. The deposited coatings have a dark anthracite-grey colour and they are hard and abrasion resistant. JE29-1 deposits uniform rhodium layers and has a strong colour consistency.The plating layer created by pen plating is very thin. If you would like a thicker layer, we recommend that you treat the goods in a normal electroplating bath.Rhodium content: 2g Rh/100 mlVoltage: 6-10 VoltBath temperature: Room temperature
Rhodium Concentrate JE88 - 2 g/100ml Rh
The rhodium concentrate JE88 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 1 µm can be deposited.Operating data:Rhodium content: 2,0 g/100ml RhpH-Value: <1Operating conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 40 °CExposition time: 2 min. (1 - max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1:1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 liters Deposition data:Hardness: 800 - 900 HVLayer thickness: max. 1,0 µmLayer density: approx. 12,4 g/cm3Form of delivery:- Ready for use 2 g/L Rh- Concentrate form 2 g/100ml Rh for 1 litre bathConcentrated bath preparation:Mix 100 ml of the Rhodium JE88 concentrate with 900 ml distilled water.
Rhodium Concentrate JE88 CLEAN - 2 g/100ml Rh
The rhodium concentrate CLEAN JE88 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. The rhodium concentrate CLEAN is produced exclusively from recycled rhodium. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 1 µm can be deposited. Operating data:Rhodium content: 2,0 g/100ml Rh pH-Value: < 1 Operating conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 40 °CExposition time: 2 min. (1 - max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1 : 1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 - 900 HV Layer thickness: max. 1,0 µm Layer density: approx. 12,4 g/cm3 Form of delivery:- Ready for use 2 g/L Rh - Concentrate form 2 g/100ml Rh for 1 litre bath Concentrated bath preparation:Mix 100 ml of the Rhodium JE88 concentrate with 900 ml distilled water.
Rhodium Concentrate JE88-1 - 1 g/100ml Rh
The rhodium concentrate JE88-1 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 0,5 µm can be deposited.Operating data:Rhodium content: 1,0 g/100ml RhpH-Value: <1Operating conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 40 °CExposition time: 2 min. (1 - max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1 : 1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 - 900 HVLayer thickness: max. 0,5 µmLayer density: approx. 12,4 g/cm3Form of delivery:- Ready for use 1 g/L Rh- Concentrate form 1 g/100ml Rh for 1 litre bathConcentrated bath preparation:Mix 100 ml of the Rhodium JE88 concentrate with 900 ml distilled water.
Rhodium concentrate JE88-1 CLEAN - 1 g/100ml Rh
The rhodium concentrate JE88-1 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. The rhodium concentrate CLEAN is produced exclusively from recycled rhodium. The color of the electrolyte in the bottle may vary slightly, as the product is made exclusively from recycled rhodium. However, this does not affect the color of the deposited rhodium layer. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 0,5 µm can be deposited. Operating data:Rhodium content: 1,0 g/100ml Rh pH-Value: < 1 Operating conditions:Voltage: 2 - 3 VoltBath temperature: 20 - 40 °CExposition time: 2 min. (1 - max. 10 min.)Anodes: platinized titanium or mixed metal oxideAnode/Cathode surface: 1 : 1Agitation: advantageousCurrent density: 0,5 - 2 A/dm2Bath filtration: from 10 litersDeposition data:Hardness: 800 - 900 HV Layer thickness: max. 0,5 µm Layer density: approx. 12,4 g/cm3 Form of delivery:- Ready for use 1 g/L Rh- Concentrate form 1 g/100ml Rh for 1 litre bath Concentrated bath preparation:Mix 100 ml of the Rhodium JE88 concentrate with 900 ml distilled water.
Rhodium Replenisher JE88 - 5g/100ml Rh
Rhodium Replenisher for Rhodiumbath JE 88. The rhodium bath JE88 deposits mirror shining, brilliant white, magnificent hard and abrasion resistant rhodium layers. It is preferably used for decorative coatings in the jewellery industry. In many cases the rhodium electrolyte is used as tarnish protection for silver products. Coatings up to 1,0 µm can be deposited.Rhodium content 5 g/100ml
Rhodium white JE28-1 for pen (1 g/50ml Rh)
The rhodium bath JE28-1 for pen is especially suitable for partial plating, for multi-colour processeing and reparation or restoration. The deposited coatings have a brilliant white colour and they are hard and abrasion resistant. JE28-1 deposits uniform rhodium layers and has a strong colour consistency.The plating layer created by pen plating is very thin. If you would like a thicker layer, we recommend that you treat the goods in a normal electroplating bath.Rhodium content: 1g Rh/50 mlVoltage: 10 - 11 VoltBath temperature: Room temperature
Rhodium white JE28-1 for pen (2 g/100 ml Rh)
The rhodium bath JE28-1 for pen is especially suitable for partial plating, for multi-colour processeing and reparation or restoration. The deposited coatings have a brilliant white colour and they are hard and abrasion resistant. JE28-1 deposits uniform rhodium layers and has a strong colour consistency.The plating layer created by pen plating is very thin. If you would like a thicker layer, we recommend that you treat the goods in a normal electroplating bath.Rhodium content: 2g Rh/100 mlVoltage: 10 - 11 VoltBath temperature: Room temperature
Rhodium baths for shiny surfaces
Rhodium electrolytes can be used to coat surfaces with a glossy white finish. The applied surfaces are particularly abrasion-resistant and are mainly used as decorative coatings for spectacle frames, watches or jewelry. Compared to conventional electrolytes, rhodium electrolytes are characterized by a particularly good scattering ability. Those who prefer dark surfaces can use black rhodium.